BW0-8027 Polyaspartic Abrasion-Resistant Floor Coating

Q: What is BW0-8027 polyaspartic floor coating used for?

BW0-8027 is used for city park plazas, electronic plants, mechanical factories, chemical plants, pharmaceutical and food industrial floors, plus outdoor yellowing-resistant and wear-resistant floor systems.

Q: Why is BW0-8027 suitable for industrial floor coating projects?

The data sheet describes a two-component polyaspartic floor coating with low-temperature curing, good leveling, strong substrate adhesion, abrasion resistance, impact resistance and chemical resistance.

Q: What mix ratio and coverage are listed for BW0-8027?

The listed mix ratio is 1:1 by weight. The theoretical coverage reference is 0.15 kg/m2 at 100 micrometers dry film thickness.

Q: What chemical resistance data is listed for BW0-8027?

The BW0-8027 data sheet lists acid resistance to 30% H2SO4 or 10% HCl for 240 h, alkali resistance to 30% NaOH for 240 h, salt resistance to 30 g/L for 240 h, salt spray resistance for 1500 h, oil resistance and 48 h waterproof testing.

Q: How can BW0-8027 be applied?

The application instructions list hand brush, roller, air spray at 0.3-0.5 MPa and airless spray at 15-20 MPa, with recommended dry film thickness of 100-200 micrometers as a topcoat.

Q: What should buyers confirm before ordering BW0-8027?

Buyers should confirm substrate condition, primer or existing coating compatibility, color and gloss requirements, chemical exposure, application method, target film thickness, site temperature and the latest TDS before ordering.

Product description

BW0-8027 polyaspartic abrasion-resistant floor coating

Use it when floor projects require abrasion resistance, impact resistance, chemical resistance, corrosion protection and stable color performance. Confirm substrate condition, coating method, mix ratio, target DFT and recoating interval before ordering. Key data to review: 1:1, 1 h, 9.3 MPa.

BW0-8027 Polyaspartic Floor Coating official product packaging image

What BW0-8027 delivers

BW0-8027 has high solid content and low viscosity, good leveling property and strong adhesion to the substrate. It can be applied by multiple coating methods and cured at a low temperature of 0°C.

Fast floor constructionLow-temperature curing performance helps shorten the construction cycle for floor coating projects.
Dense smooth filmAfter curing, the coating forms a dense and smooth film that helps isolate corrosive media.
Substrate adhesionStrong adhesion and good compatibility with polyurethane, epoxy and other coating films.
Outdoor durabilityUV resistance, no yellowing, no powdering and aging resistance support weathering and gloss retention.

Technical advantages for industrial floor protection.

Documented product advantages include high solids, good leveling, high hardness, scratch resistance, stain resistance, abrasion resistance, impact resistance, anticorrosion performance and direct-to-metal application capability.

0°CLow-temperature curing. Cures at low temperature to help shorten the construction cycle for floor coating projects.

5 mgAbrasion resistance. Abrasion loss under 750 g / 500 r test conditions, supporting wear-resistant industrial floor service.

50 kg·cmImpact resistance. Impact resistance result for floors exposed to equipment movement, traffic and mechanical service.

1500 hSalt spray resistance. Salt spray resistance test result with no rust, bubbles or peeling, supporting anticorrosion protection.

Application scope

Typical use areas for BW0-8027.

Flooring for city park plazas, electronic plants, mechanical factories, chemical plants, pharmaceutical facilities, food industry floors and outdoor yellowing-resistant wear-resistant floors.

Product features

High solids and low densityGood leveling with a tough, dense, full-gloss coating film and bright colors.
High hardnessGood scratch resistance and stain resistance for floor coating service.
Chemical resistanceExcellent anticorrosion property, with resistance to acid, alkali, salt and other media.
Environment-friendly formulaContains no benzene solvents and lead compounds according to the data sheet.

Project fit

BW0-8027 supports industrial floor systems requiring abrasion resistance, color retention and weatherability. Final suitability should be verified through project-specific testing and application review.

Substrate reviewConfirm surface preparation, moisture condition, primer compatibility and existing coating compatibility before application.
Service condition reviewMatch film thickness, chemical exposure, traffic load and application method to the project specification.

Product information & technical data

Technical data for BW0-8027 polyaspartic floor coating.

Review product information, physical properties and chemical resistance data for BW0-8027 in a cleaner table structure optimized for technical comparison and procurement review.

Product information

Item	A component	B component
Appearance	Light yellow liquid	Color adjustable
Specific gravity (g/cm³)	1.04	1.50
Viscosity (cps) @ 25°C	40-60	100-200
Solid content (%)	65	88
Mix ratio (by weight)	1	1
Surface dry time (h)	1
Pot life (min) @ 25°C	40
Theoretical coverage (DFT)	0.15 kg/m² film thickness 100 μm

Physical properties

Item	Test standard	Result
Pencil hardness	-	2H
Adhesion force (metal base)	HG / T 3831-2006	9.3 MPa
Adhesion force (concrete base)	HG / T 3831-2006	2.8 MPa
Bending resistance (cylindrical)	-	≤1 mm
Impermeability	-	2.1 MPa
Abrasion resistance (750 g / 500 r) / mg	HG / T 3831-2006	5
Impact resistance kg·cm	GB / T 1732	50
Anti-aging, artificial accelerated aging	GB / T 14522-1993	Light loss < 1, pulverization < 1

Chemical resistance

For reference: chemical medium resistance performance is obtained according to GB / T 9274-1988 test methods. Pay attention to ventilation, splash and spillage. Independent immersion testing is recommended if other specific data is required.

Exposure item	Result
Acid resistance 30% H₂SO₄ or 10% HCl, 240 h	No rust, no bubbles, no peel off
Alkali resistance 30% NaOH, 240 h	No rust, no bubbles, no peel off
Salt resistance 30 g/L, 240 h	No rust, no bubbles, no peel off
Salt spray resistance 1500 h	No rust, no bubbles, no peel off
Oil resistance, 0# diesel, crude oil	No rust, no bubbles, no peel off
Waterproof, 48 h	No bubbles, no wrinkles, no color change, no peel off

Application environment & guide

Application conditions, coating methods and recoat guidance.

Check temperature, humidity, dew point, application method, film thickness and recoating interval before installation.

Processing recommendation

Condition	Requirement
Environment temperature	-5°C to +35°C
Humidity	≤85%
Dew point	≥3°C

Application instructions

Guide item	Recommendation
Brush / roller application	Hand brush or roller
Air spray	Air pressure 0.3-0.5 MPa
Airless spray	Spray pressure 15-20 MPa
Recommended DFT	100-200 μm as topcoat
Recoating interval	Minimum 2 h, maximum 24 h

Application tips

Agitate Part B uniformly prior to application.
Strictly mix the two parts at the correct ratio and agitate uniformly.
Seal the package well after use to avoid moisture absorption.
Keep the application site clean and dry; avoid contact with water, alcohols, acids and alkali.

Curing time, shelf life and packing

Curing time, storage and packing information for project planning.

Use the curing profile, shelf-life data and packing details below to plan application timing, warehouse handling and bulk project purchasing.

Product curing time

Note: curing time varies with environmental conditions, especially temperature and relative humidity.

Substrate temperature	Surface dry time	Foot traffic / Solid dry time
+10°C	2 h	24 h / 7 d
+20°C	1.5 h	8 h / 7 d
+30°C	1 h	6 h / 7 d

Shelf life & packing

Item	Details
Shelf life from manufacturing date	Part A: 10 months · Part B: 10 months
Storage temperature	+5°C to +35°C
Package requirement	Keep the package drum well sealed
Storage precaution	Store in a cool, ventilated place and avoid sunshine exposure
Package	Part A: 20 kg / barrel · Part B: 20 kg / barrel

Health & safety / integrity declaration

Safety data, handling guidance and application verification.

Product health and safety information

For information and advice on the safe handling, storage and disposal of chemical products, users shall refer to the most recent Material Safety Data Sheet containing physical, ecological, toxicological and other safety-related data.

Integrity declaration

Colorful Whale Advanced Materials (Shanghai) Co., Ltd. guarantees all technical data stated in this sheet are based on laboratory tests. Actual testing methods may vary due to different circumstances. Therefore please test and verify its applicability. Colorful Whale Advanced Materials (Shanghai) Co., Ltd. assumes no responsibility except for product quality and reserves the right of any modifications on the listed data without prior notice.

FAQ

FAQ about BW0-8027 polyaspartic floor coating.

These answers support engineering review, contractor planning and bulk project purchasing before ordering.

What is BW0-8027 polyaspartic floor coating used for?

BW0-8027 is used for city park plazas, electronic plants, mechanical factories, chemical plants, pharmaceutical and food industrial floors, plus outdoor yellowing-resistant and wear-resistant floor systems.

Why is BW0-8027 suitable for industrial floor coating projects?

The data sheet describes a two-component polyaspartic floor coating with low-temperature curing, good leveling, strong substrate adhesion, abrasion resistance, impact resistance and chemical resistance.

What mix ratio and coverage are listed for BW0-8027?

The listed mix ratio is 1:1 by weight. The theoretical coverage reference is 0.15 kg/m2 at 100 micrometers dry film thickness.

What chemical resistance data is listed for BW0-8027?

The BW0-8027 data sheet lists acid resistance to 30% H2SO4 or 10% HCl for 240 h, alkali resistance to 30% NaOH for 240 h, salt resistance to 30 g/L for 240 h, salt spray resistance for 1500 h, oil resistance and 48 h waterproof testing.

How can BW0-8027 be applied?

The application instructions list hand brush, roller, air spray at 0.3-0.5 MPa and airless spray at 15-20 MPa, with recommended dry film thickness of 100-200 micrometers as a topcoat.

What should buyers confirm before ordering BW0-8027?

Buyers should confirm substrate condition, primer or existing coating compatibility, color and gloss requirements, chemical exposure, application method, target film thickness, site temperature and the latest TDS before ordering.

Request technical documents

Explore polyurea products Polyaspartic coatings Contact technical support

Request TDS, application guidance or bulk project support.

If you are evaluating BW0-8027 for industrial flooring, outdoor wear-resistant floors or corrosion-resistant floor coating work, request the latest technical data sheet, application guidance and project-specific compatibility review before ordering.